Ti-20V-4Al-1Sn合金の機械的性質に及ぼす冷間圧延と短時間時効処理の影響 Influence of Cold-Rolling and Short-Time Aging on Mechanical Properties of Ti-20V-4Al-1Sn Alloy

この論文にアクセスする

この論文をさがす

著者

抄録

  This study was conducted to examine the effect of aging treatment for a short time between 6 s and 1.8 ks after cold-rolling on the mechanical properties of the β titanium alloy Ti-20V-4Al-1Sn. Cold-rolling at between 30% and 70% reduction accelerated hardening with aging at 673 K. It was thought that the dislocations introduced during cold-rolling provided suitable places for α fine-phase precipitation. When the alloy was cold-rolled at 70% reduction and then aged at between 673 K and 823 K by induction heating, the α phase precipitation occurred from 6 s and its volume fraction increased with time. As the aging temperature was lower and the aging time was longer, the average distance between the particles of the precipitated α phase became small, so that hardness and tensile strength increase was remarkable. In particular, the tensile strength of the alloy was significantly improved to 1510 MPa by aging for 1.8 ks at 723 K after cold-rolling at 70% reduction although ductility was greatly decreased.<br>

収録刊行物

  • 日本金屬學會誌 = Journal of the Japan Institute of Metals  

    日本金屬學會誌 = Journal of the Japan Institute of Metals 70(10), 797-803, 2006-10-20 

    The Japan Institute of Metals

参考文献:  27件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018310657
  • NII書誌ID(NCID)
    AN00062446
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    00214876
  • NDL 記事登録ID
    8550590
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-314
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ