Preparation and Evaluation of Uniform-size (-)-Ephedrine-imprinted Polymeric Microspheres by Multi-step Swelling and Suspension Polymerization
-
- LI Yingchun
- Department of Pharmacy, School of Medicine, Xi'an Jiaotong University
-
- FU Qiang
- Department of Pharmacy, School of Medicine, Xi'an Jiaotong University
-
- ZHANG Qianqian
- Department of Pharmacy, School of Medicine, Xi'an Jiaotong University
-
- HE Langchong
- Department of Pharmacy, School of Medicine, Xi'an Jiaotong University
この論文をさがす
抄録
Ephedrine-imprinted polymeric microspheres have been prepared in an aqueous system by multi-step swelling and suspension polymerization, using methacrylic acid (MAA) as a functional monomer, and ethylene glycol dimethacrylate (EGDMA) as a cross-linker. Scanning electron microscopy (SEM) was used as a means to identify the structure features of the obtained polymers. Further, we examined the recognition mechanism of the polymers and the influences of some chromatographic conditions, such as the mobile-phase composition, flow-rate, column temperature and sample amount on the retentivity and selectivity for (-)-ephedrine and (+)-ephedrine. The results reveal that stable macroporous polymer beads with good size monodispersity were obtained, the average size of which was 3 - 5 µm. Baseline chiral separation of the template isomers was achieved on a short column (50 mm × 4.6 mm i.d.) when the prepared polymer beads were used as a stationary phase, while the non-imprinted polymers (NIPs) did not show such ability. The optimized chromatographic condition was as follows: acetonitrile-acetic acid (99.8/0.2, v/v) as the mobile phase; sample amount, 40 - 80 µg; flow rate, 1.0 ml min-1; and column temperature, room temperature, respectively. It is assumed that two classes of binding sites exist in the porous polymers, one being hydrophilic binding sites, the other being hydrophobic binding sites.
収録刊行物
-
- Analytical Sciences
-
Analytical Sciences 22 (10), 1355-1360, 2006
社団法人 日本分析化学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679235095936
-
- NII論文ID
- 130004441188
- 10018322012
-
- NII書誌ID
- AA10500785
-
- ISSN
- 13482246
- 09106340
-
- NDL書誌ID
- 8080400
-
- Web Site
- https://ndlsearch.ndl.go.jp/books/R000000004-I8080400
- https://link.springer.com/content/pdf/10.2116/analsci.22.1355.pdf
- https://link.springer.com/article/10.2116/analsci.22.1355/fulltext.html
- http://www.jstage.jst.go.jp/article/analsci/22/10/22_10_1355/_pdf
- https://search.jamas.or.jp/link/ui/2007042799
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可