- Fabrication of Thin Palladium Membrane by Electroplating Coexisting with Supercritical Carbon Dioxide
- チョウリンカイ 2サンカタンソ キョウゾン カ デ ノ デンキメッキ ニ ヨル パラジウム ハクマク ノ サクセイ
この論文をさがす
抄録
A supported thin palladium membrane was fabricated using electroplating coexisting with supercritical carbon dioxide, named supercritical electroplating. In this unique electroplating, immediate dissolution of hydrogen formed via water electrolysis into supercritical carbon dioxide as well as fabrication of a dense metallic film consisting of nano-size crystals will be expected by dispersion of conductive plating solution into inconductive supercritical carbon dioxide. Commercially available palladium plating baths, however, cannot be applied to supercritical electroplating aqueous solution with acidic property, because they were developed to extend the service life by the formation of stable palladium complex in ammonium aqueous solution with basic property. In this study, a new bath composed of PdCl2, KBr, KNO2, H3BO3, Glycine and surfactant was developed for the supercritical palladium plating. As a result, a defect-free palladium film could be fabricated on a porous conductive support.
収録刊行物
-
- 膜
-
膜 31 (6), 332-336, 2006
日本膜学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206421383808
-
- NII論文ID
- 10018407456
-
- NII書誌ID
- AN0023215X
-
- ISSN
- 18846440
- 03851036
- http://id.crossref.org/issn/03851036
-
- NDL書誌ID
- 8588673
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可