酸化ジルコニウム被覆酸化チタン粉末の作製およびその性質 Preparation and Properties of Zirconium Oxide-Coated Titanium Oxide Powder

この論文にアクセスする

この論文をさがす

著者

抄録

ZrO<SUB>2</SUB>-coated TiO<SUB>2</SUB> powder was prepared using zirconium tetra-n-butoxide through the sol-gel method. Specific surface area and photocatalytic activity of ZrO<SUB>2</SUB>-coated TiO<SUB>2</SUB> powder was measured. Crystalline phase of ZrO<SUB>2</SUB>-coated TiO<SUB>2</SUB> powder was investigated. Specific surface area, crystalline phase and catalytic activity depended on amount of ZrO<SUB>2</SUB>-coated. The photocatalytic activity of TiO<SUB>2</SUB> powder was decreased with increasing heat-treatment temperature at the range from 400°C to 800°C. The photocatalytic activity of 1 mass% ZrO<SUB>2</SUB>-coated TiO<SUB>2</SUB> powder was higher than that of uncoated TiO<SUB>2</SUB> powder after the heattreatment at 400°C, 600°C and 800°C, respectively. It is considered that sintering of heated TiO<SUB>2</SUB> powder is depressed by coated ZrO<SUB>2</SUB>.

収録刊行物

  • Journal of the Society of Inorganic Materials, Japan : セッコウ・石灰・セメント・地球環境の科学  

    Journal of the Society of Inorganic Materials, Japan : セッコウ・石灰・セメント・地球環境の科学 14(328), 141-145, 2007-05-01 

    The Society of Inorganic Materials, Japan

参考文献:  6件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018419896
  • NII書誌ID(NCID)
    AA11416367
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    13453769
  • NDL 記事登録ID
    8813522
  • NDL 雑誌分類
    ZP9(科学技術--化学・化学工業--無機化学・無機化学工業--セラミックス・窯業)
  • NDL 請求記号
    Z17-B79
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ