Prediction of Phase Separation in Silicate Glass for the Creation of Value-added Materials from Waste Slag

• Suzuki Masanori

  Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University

• Tanaka Toshihiro

  Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University

抄録

A thermodynamic evaluation was performed to predict phase separation in multi-component oxide glasses. Composition ranges for metastable liquid–liquid immiscibility and spinodal decomposition in a SiO₂–CaO–MgO–Na₂O quaternary system were calculated on the assumption that glasses in the oxide system can be regarded as super-cooled liquid phases. Some experimental studies on two-phase separation of glasses were carried out to confirm the thermodynamic evaluation of the phase separation. Microstructures in heat-treated glass samples were observed by transmission electron microscopy, to investigate the development of interconnected microstructures in the glass with increased heating temperatures and holding times, and spinodal decomposition of glass was indicated.

収録刊行物

• ＩＳＩＪ　Ｉｎｔｅｒｎａｔｉｏｎａｌ

  ＩＳＩＪ　Ｉｎｔｅｒｎａｔｉｏｎａｌ 46 (10), 1391-1395, 2006

  一般社団法人 日本鉄鋼協会

キーワード

• spinodal decomposition
• SiO₂–CaO–MgO–Na₂O system
• Gibbs energy
• thermodynamic databases
• super-cooled liquid phase

詳細情報

• CRID: 1390001206489452288
• NII論文ID: 10018425962
• NII書誌ID: AA10680712
• DOI: 10.2355/isijinternational.46.1391
• ISSN: 13475460
• ISSN: 09151559
• HANDLE: 11094/26396
• Web Site: http://www.jstage.jst.go.jp/article/isijinternational/46/10/46_10_1391/_pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • IRDB
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可