偏光近接場光学顕微鏡を用いた相互侵入球晶の観察 The Observation of Interpenetrated Spherulites by Polarized Scanning Near-field Optical Microscopy

この論文にアクセスする

この論文をさがす

著者

    • 栗間 昭宏 KURIMA Akihiko
    • 東京工業大学大学院理工学研究科有機・高分子物質専攻 Department of Organic and Polymeric Materials, Graduate School of Science and Engineering, Tokyo Institute of Technology
    • 中嶋 健 NAKAJIMA Ken
    • 東京工業大学大学院理工学研究科有機・高分子物質専攻 Department of Organic and Polymeric Materials, Graduate School of Science and Engineering, Tokyo Institute of Technology
    • 西 敏夫 NISHI Toshio
    • 東京工業大学大学院理工学研究科有機・高分子物質専攻 Department of Organic and Polymeric Materials, Graduate School of Science and Engineering, Tokyo Institute of Technology

抄録

結晶性/結晶性ポリマーブレンドにおける相互侵入球晶 (interpenetrated spherulites : IPS) は異種の高分子どうしの球晶が衝突しても界面を形成せず, 一方が他方に侵入して成長を続けるという興味深いものである. poly(butylene succinate)/poly(ethylene oxide) (PBSU/PEO) は高融点成分PBSUが先に結晶化し, その後低融点成分PEOがPBSU球晶内に相互侵入しながら結晶化することが偏光顕微鏡の観察によりわかっている. このような相互侵入球晶の結晶化機構をより深く理解するために光学像と表面凹凸像を同時に得られる利点をもつ偏光近接場光学顕微鏡 (polarized scanning near-field optical microscopy : polarized SNOM) を使い, その結晶化をその場観察した. その結果, PBSUにPEOが侵入することで表面の消光リングの凹凸構造が大きくなり, それによってレターデーションが大きくなることが確かめられた.

Some miscible crystalline/crystalline polymer blends show an interesting phenomenon that one spherulite grows through the interlamellar regions of another spherulite; this process is called interpenetrated spherulite (IPS) formation. For example, poly(butylenes succinate)/poly(ethylene oxide) (PBSU/PEO) is one of the non-simultaneous IPS systems, where PBSU at first crystallizes during rapid cooling and PEO goes on growing and penetrating into PBSU spherulites at isothermal condition even after collision. IPS formation has already been examined using polarizing optical microscopy (POM). The increase in birefringence of the area of PBSU spherulites was the evidence of IPS. However, the detailed crystallization mechanism could not be well understood due to the poor resolution that was restricted by the diffraction limit. In this paper, we report the result of <i>in situ</i> observation of IPS formation by polarized scanning near-field optical microscopy (SNOM), which has higher optical resolution, beyond the diffraction limit, and simultaneous topographic imaging capability. The increase in topographic unevenness and simultaneous retardation increase were directly observed. We speculate that the result was due to the crystalline growth of PEO along PBSU twisted lamellae.

収録刊行物

  • 高分子論文集  

    高分子論文集 63(12), 774-780, 2006-12-25 

    The Society of Polymer Science, Japan

参考文献:  17件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018457949
  • NII書誌ID(NCID)
    AN00085011
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    03862186
  • NDL 記事登録ID
    8625653
  • NDL 雑誌分類
    ZP16(科学技術--化学・化学工業--高分子化学・高分子化学工業)
  • NDL 請求記号
    Z17-92
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ