- Hung T. H.
- Institute of Materials Science and Engineering; Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University
-
- Huang J. C.
- Institute of Materials Science and Engineering; Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University
-
- Jang J. S. C.
- Department of Materials Science and Engineering, I-Shou University
-
- Lu S. C.
- Department of Materials Science and Engineering, I-Shou University
この論文をさがす
抄録
Both the glass forming ability and thermal stability of the Zr65-x-yAl7.5Cu17.5Ni10 amorphous alloy can be improved by the appropriate addition of Si and B. The metalloid elements would extend the nucleation stage and result in more small crystalline particles. The basic crystallization kinetics for the Si/B containing alloys is still similar to the base alloy, but would proceed at a higher temperature or a more sluggish speed.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (2), 239-243, 2007
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227362048
-
- NII論文ID
- 10018508901
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8623842
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可