Structural Changes of Precipitates in an Mg-5 at%Gd Alloy Studied by Transmission Electron Microscopy
-
- Nishijima Masahiko
- Institute for Materials Research, Tohoku University
-
- Hiraga Kenji
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Structural Changes of Precipitates in an Mg 5 atパーセントGd Alloy Studied by Transmission Electron Microscopy
この論文をさがす
抄録
Structural changes of precipitates in an Mg-5 at%Gd (Mg95Gd5) alloy by aging at 200°C and 250°C have been studied by ordinary high-resolution transmission electron microscopy (HRTEM) and high-angle annular detector dark-field scanning transmission electron microscopy (HAADF-STEM). In the early stage of precipitation by aging at 200°C up to 5 h, a short-range ordered structure exists in Gd-enriched regions with an about 2 nm size, and nuclei of an Mg7Gd structure (β′ phase) occur in the short-range ordered structure by aging at 200°C for 5 h. The β′ phase with the Mg7Gd structure is formed as definite precipitates by aging at 200°C for 10 h. The β′ precipitates are joined along the b-axis and form a plate-shape with a thickness of about 20 nm along the a-axis, and lengths of about 200 nm along the b-axis and 200 nm along the c-axis, and the connection of planar precipitates along the three directions, which are parallel to the [210]m-typed directions of the Mg-matrix, forms a two-dimensional cell structure, by top-aging at 200°C for 100 h.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (1), 10-15, 2007
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204249446784
-
- NII論文ID
- 130004453330
- 10018665955
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2sXit1Whs7s%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8597164
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可