Determination of Cyclic-Tension Fatigue of Al-4Cu-1Mg Alloy Using Ultrasonic Shear Waves

  • Yamagishi H.
    Central Research Institute, Toyama Industrial Technology Center
  • Fukuhara M.
    Institute for Materials Research, Tohoku University

Search this article

Abstract

Cyclic-tension fatigue of aluminum alloy, Al-4Cu-1Mg, was determined by an analysis of diffracted SH and SV waves, passing through the surface and reflecting the bottom of the specimen, respectively. The propagation time of SH waves and the internal friction of SV waves begins to decrease and increase from fatigue damage ratio (=NNf) of 0.5, respectively, suggesting noticeable increase of movable dislocation. From the analysis of SH waves along the direction to the loading axis, the damping ratio decreases and the phase advances with increasing of the degree of fatigue. Assumed from SH wave flux model, the former behavior correlates well with increasing of the residual stress by cyclic tension. The latter may be characterized by viscoelasticity. These results show that ultrasonic transmission method is useful probe for evaluation of fatigue in aluminum alloy.

Journal

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 48 (3), 550-555, 2007

    The Japan Institute of Metals and Materials

Citations (2)*help

See more

References(35)*help

See more

Details

Report a problem

Back to top