摩擦圧接した管状球状黒鉛鋳鉄の組織と機械的性質

• 晴山 巧

  山形県工業技術センター

• 新田 拓也

  新東工業(株)

• 堀江 皓

  岩手大学工学部

書誌事項

タイトル別名

• Microstructure and Mechanical Properties of Pipe Shaped Spheroidal Graphite Cast Iron Bonded by Friction Welding Method
• マサツ アッセツシタ カンジョウ キュウジョウ コクエン チュウテツ ノ ソシキ ト キカイテキ セイシツ

抄録

  Friction welding of pipe shaped spheroidal graphite cast iron was carried out under welding conditions such as peripheral speed (rotational speed), friction pressure, friction time and forge pressure. The dimensions of the test pieces were 42mm in outside diameter and 28mm in inside diameter respectively. As a result, tensile strength increased with increasing peripheral speed, friction pressure, friction time, and forge pressure. High tensile strength specimens were broken on the base metal. On the other hand, tensile strength decreased with increasing layer of deformed spheroidal graphite.

収録刊行物

• 鋳造工学

  鋳造工学 79 (3), 146-150, 2007

  公益社団法人 日本鋳造工学会

キーワード

• spheroidal graphite
• cast iron
• pipe
• friction welding
• microstructure
• mechanical property

詳細情報

• CRID: 1390282681485283456
• NII論文ID: 10018851423
• NII書誌ID: AN10514770
• DOI: 10.11279/jfes.79.146
• COI: 1:CAS:528:DC%2BD2sXktFOktbk%3D
• ISSN: 21855374
• ISSN: 13420429
• NDL書誌ID: 8738094
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I8738094
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可