Thin Film of Silica Nanoparticles with Highly Ordered Hemispherical Macropores

この論文にアクセスする

この論文をさがす

著者

抄録

A thin film of silica nanoparticles with highly ordered hemispherical macropores and an ordering factor, <I>Ø</I><SUB>VP6</SUB>, of 98% was proved to be obtained by the Voronoi polygon analysis. Firstly, a monolayer of submicron polystyrene latex particles (PSL) with silica nanoparticles is obtained by coating a binary suspension of PSL particles and silica nanoparticles on a glass substrate using a spin coater. Secondly, the PSL particles are completely decomposed by calcining the coated films at 400°C for 10 min, affording a thin film of silica nanoparticles with hemispherical macropores. The size of the hemispherical macropores can be controlled from 136 to 506 nm by choosing PSL particles as a template. Although the monolayer of PSL particles without silica nanoparticles has several point and line defects, the PSL particle monolayer with silica nanoparticles has few defects. The small size of the silica nanoparticles is preferable for highly ordered hemispherical macropores. We propose a model that explains the ordering mechanism of particles during drying. The thin film of highly ordered hemispherical macropores can be used as a template for microcontact printing due to its hemispherical shape, or as an anti-reflective film due to its optical properties.

収録刊行物

  • Journal of chemical engineering of Japan  

    Journal of chemical engineering of Japan 40(4), 341-347, 2007-04-01 

    The Society of Chemical Engineers, Japan

参考文献:  23件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10018902514
  • NII書誌ID(NCID)
    AA00709658
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    00219592
  • NDL 記事登録ID
    8705819
  • NDL 雑誌分類
    ZP1(科学技術--化学・化学工業)
  • NDL 請求記号
    Z53-R395
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ