書誌事項
- タイトル別名
-
- Preparation of the Fe-based Glassy Alloy Powder Cores and their Applications
- Feキ キンゾク ガラス フンマツ オ モチイタ アップン ジシン ノ サクセイ ト オウヨウ
この論文をさがす
抄録
New core (LiqualloyTM core) made of soft magnetic Fe-based glassy alloy powder was fabricated by the consolidation using an uni-axial mechanical press at room temperature. This new core has the constant relative permeability (μ') of about 60 up to 1 MHz and extremely low core loss blow 200kW/m3 at f=100kHz and Bm=0.1 T. The efficiency of the switching power supply (η) was improved by 2∼3% when the LiqualloyTM core was used instead of Fe-Al-Si core. The temperature rise near the LiqualloyTM core (ΔT) was also 10K lower than that of the Fe-Al-Si core. These excellent properties of the LiqualloyTM core are based on its extremely low hysteresis and eddy current losses. These low losses are originated from its good soft magnetic properties (Hc=2A/m) after annealing at relatively low temperature, its intrinsic hardness (Hv=1000) and high resistivitiy (ρ=160μΩcm).
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 54 (11), 768-772, 2007
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206307126912
-
- NII論文ID
- 10019983377
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BD2sXhtlCksr3N
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 9279337
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可