Effects of Ag addition on microstructure and thermoelectric properties of NaxCo2O4 synthesized by citric acid complex process
-
- Ito Mikio
- Course of Materials Science and Engineering, Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
-
- Furumoto Daisuke
- Course of Materials Science and Engineering, Division of Materials and Manufacturing Science, Graduate School of Engineering, Osaka University
書誌事項
- タイトル別名
-
- Effects of Ag Addition on Microstructure and Thermoelectric Properties of Na<I><SUB>x</SUB></I>Co<SUB>2</SUB>O<SUB>4</SUB> Synthesized by Citric Acid Complex Process
この論文をさがす
抄録
A thermoelectric NaxCo2O4/Ag composite was synthesized by citric acid complex process using CH3COOAg as an Ag source. The powder precursor after calcination was composed of plate-like NaxCo2O4 grains and Ag particles. The Ag addition deteriorated crystallographic anisotropy of the sintered body. However, the electrical resistivity and the Seebeck coefficient of this composite were significantly smaller and slightly larger, respectively, than those of the sample without Ag, resulting in lager power factor. The Ag phase dispersed in the NaxCo2O4 matrix contained about 5–17 at.% Co, which is considered to cause the increase in Seebeck coefficient.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (12), 3160-3163, 2007
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204250827392
-
- NII論文ID
- 10020008089
- 130004453454
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9280572
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可