純ニオブの水素化にともなう局所格子ひずみと化学結合の変化

• 南部 智憲

  鈴鹿工業高等専門学校材料工学科

• 江崎 尚和

  鈴鹿工業高等専門学校材料工学科

• 湯川 宏

  名古屋大学大学院工学研究科マテリアル理工学専攻

• 森永 正彦

  名古屋大学大学院工学研究科マテリアル理工学専攻

書誌事項

タイトル別名

• Local Lattice Distortion and Chemical Bond Change during Hydrogenation in Pure Niobium
• ジュンニオブ ノ スイソカ ニ トモナウ キョクショ コウシ ヒズミ ト カガク ケツゴウ ノ ヘンカ

抄録

  The local lattice distortion and the chemical bond change in the course of hydrogenation in niobium metal were simulated using the pseudopotential method and the DV-Xα molecular orbital method. The calculated enthalpy changes, ΔH, of hydrogen solution into niobium indicated that hydrogen could be dissolved readily into niobium up to the hydrogen content (H/M) of about 0.7 at 673 K, but further dissolution became difficult, in agreement with the experiment. The local lattice distortion appeared to occur in the niobium lattice so as to suppress the large decrease in the Nb-Nb covalent interaction during hydrogen dissolution, while enhancing the Nb-H interaction.<br>

収録刊行物

• 日本金属学会誌

  日本金属学会誌 70 (7), 541-547, 2006

  公益社団法人 日本金属学会

キーワード

• pseudopotential method
• DV-Xα cluster method
• enthalpy of hydrogen solution
• niobium
• niobium hydride

詳細情報

• CRID: 1390282681455568768
• NII論文ID: 130004455720
• NII論文ID: 10020523713
• NII書誌ID: AN00187860
• DOI: 10.2320/jinstmet.70.541
• ISSN: 18806880
• ISSN: 24337501
• ISSN: 00214876
• NDL書誌ID: 8042137
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I8042137
• Web Site: https://www.jstage.jst.go.jp/article/jinstmet/70/7/70_7_541/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可