８ｍａｓｓ％Ｙ２Ｏ３・ＺｒＯ２／ＣｏＮｉＣｒＡｌＹ遮熱コーティングの高温加熱による酸化およびトップコートのはく離

DOI Web Site 被引用文献6件 参考文献14件

書誌事項

タイトル別名
  • Oxidation of 8mass%Y2O3 ZrO2/CoNiCrAlY Thermal Barrier Coating by Heating at High Temperature and Delamination of Top Coat.
  • 8massパーセントY2O3 ZrO2 CoNiCrAlYシャネツ コーティング ノ コウオン カネツ ニ ヨル サンカ オヨビ トップコート ノ ハクリ

この論文をさがす

抄録

Thermal barrier coating (TBC) was applied on the Co based superalloy specimens, where CoNiCrAlY bond coat was deposited by high velocity oxygen fuel (HVOF) spraying and 8mass% yttria stabilized zirconia (YSZ) top coat by atmospheric plasma spraying. The isothermal oxidation behavior of TBC at high temperature was characterized by scanning electron microscopy, EPMA mapping analysis, energy dispersive spectroscopy and X-ray diffraction. The Alumina and complex oxide layers were formed along the interface between the top coat and the bond coat, and the thickness of the oxide layers increased with increasing heating temperature and holding time. When the delamination of the top coat occurred during the holding of the specimen at 1473K for 1732ks and on cooling after holding at 1273K for 3960ks, half-sphere-shaped cracks grew along the interface between unmelted bond coat particles and Al2O3 layer, and propagated in the complex oxide or the top coat. In tensile test and edge-indent test, the delamination of top coat started near the top of particles and extended in the top coat under shear stress.

収録刊行物

  • 材料

    材料 51 (1), 95-100, 2002

    公益社団法人 日本材料学会

被引用文献 (6)*注記

もっと見る

参考文献 (14)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ