A Plate-Type Anodic Alumina Supported Nickel Catalyst for Methane Steam Reforming
-
- Zhou Lu
- Department of Chemical Engineering, Tokyo University of Agriculture and Technology
-
- Guo Yu
- Department of Chemical Engineering, Tokyo University of Agriculture and Technology
-
- Zhang Qi
- Department of Chemical Engineering, Tokyo University of Agriculture and Technology
-
- Tran Thanh Phong
- Department of Chemical Engineering, Tokyo University of Agriculture and Technology
-
- Sakurai Makoto
- Department of Chemical Engineering, Tokyo University of Agriculture and Technology
-
- Kameyama Hideo
- Department of Chemical Engineering, Tokyo University of Agriculture and Technology
この論文をさがす
抄録
An anodic alumina supported nickel catalyst (Ni/Al2O3/Alloy) was synthesized using a double impregnation method with a high temperature calcination in between, to investigate reactivity performance thereof during steam reforming of methane (SRM) reactions in continuous and daily start-up and shut-down (DSS)-like operations. The catalyst was structurally characterized using X-ray diffraction (XRD), BET and temperature programmed reduction (TPR) technologies. The TPR results showed that almost all nickel content from the first impregnation was transformed into nickel aluminate, whereas nickel from the second impregnation predominantly existed in the more reducible forms of NiO and xNiO·Al2O3 (x < 1). The existence of these NiO and NiAl2O4 phases was identified by XRD.<BR>The catalyst provided high and stable SRM reactivity near the equilibrium value, while no deactivation was observed in continuous durability testing for 200 h at 800°C and 130 h at 700°C, and in DSS-like mode operation at 700°C. The investigation of the influence of methane and/or steam treatments on the reactivity of Ni/Al2O3/Alloy showed the catalyst is not disturbed by the methane treatment, whereas it is remarkably deactivated by the steam treatment. In addition, no differences in the reduction effect were found when using hydrogen or methane to regenerate a steamed catalyst.
収録刊行物
-
- JOURNAL OF CHEMICAL ENGINEERING OF JAPAN
-
JOURNAL OF CHEMICAL ENGINEERING OF JAPAN 41 (2), 90-99, 2008
公益社団法人 化学工学会
- Tweet
詳細情報
-
- CRID
- 1390282679546558336
-
- NII論文ID
- 10021109642
-
- NII書誌ID
- AA00709658
-
- ISSN
- 18811299
- 00219592
-
- NDL書誌ID
- 9383968
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可