Observation of Beta Phase Particles in an Isothermally Aged Al-10mass%Mg Alloy with and without 0.5mass%Ag

この論文にアクセスする

この論文をさがす

著者

抄録

Characterization of the β′ and β precipitate phases formed in the aged Al-10 mass%Mg alloy with and without 0.5 mass%Ag at 200°C and 240°C has been carried out using TEM. The plate-like precipitate particles were formed in binary alloys aged from 2 h at 200°C. The plate-like particles had habit planes of {100}<SUB>α</SUB>, and were identified as the β′ phase. Whereas the very fine scale, uniformly distributed precipitate particles with a spherical shape were formed as the dominant precipitate particle in ternary alloy aged at 200°C for periods of 4 h and 6 h. These small spherical particles were identified to be icosahedral phase while no icosahedral phase was observed in the Ag-free alloys when samples were aged at 200°C. Formation of a precipitate cluster consisting of two distinguishable parts has been observed in binary alloys aged 5 h at 240°C, and these precipitate particles were identified as the equilibrium β and metastable β′ phases. Whereas a higher volume fraction of dispersed precipitate phases which comprised a mixture of a coarse-scale, rod-like particles and blocky particles, was observed in ternary alloy aged 5 h at 240°C. With further increase of ageing time up to 24 h at 240°C, the microstructure contained a high volume fraction of coarse-scale, globular precipitate particles, together with a secondary distribution of fine-scale spheroidal precipitates, these coarse globular particles were identified to be the equilibrium β phase.

収録刊行物

  • Materials transactions  

    Materials transactions 49(2), 235-241, 2008-02-01 

    The Japan Institute of Metals and Materials

参考文献:  20件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10021143956
  • NII書誌ID(NCID)
    AA1151294X
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    13459678
  • NDL 記事登録ID
    9354205
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z53-J286
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ