Low Temperature Isothermal Reduction Kinetics of Fe_2O_3/NiO Mixed Oxides and Comparative Synthesis of Fe_<1-x>Ni_x Alloys

この論文にアクセスする

この論文をさがす

著者

抄録

Two Molar ratios 1:1 and 1:2 of AR grade nickel oxide and iron oxide powder was mixed and compacted. The fired compacts were isothermally reduced in pure hydrogen at 500, 550, 600 and 650°C. Based on thermogravimetric analysis, the reduction behavior and kinetics reaction mechanism were studied comparatively for the different mixed oxides ratios. The initial fired powder and the various reduction products were characterized by XRD, SEM, TEM and reflected light microscope to reveal the effect of hydrogen reduction on composition and microstructure of produced Ferronickel alloy. Synthesis of nanocrystalline Fe<SUB>1−<I>x</I></SUB>Ni<I><SUB>x</SUB></I> alloy with 33 and 20 at% Ni for reduction of 1:1 and 1:2 NiO/Fe<SUB>2</SUB>O<SUB>3</SUB> ratios was detected respectively. The activation energy values were calculated from Arrhenius equation and the approved mathematical formulations for the gas solid reaction were applied. It was found that for NiO/Fe<SUB>2</SUB>O<SUB>3</SUB> of both 1:1 and 1:2 ratios, the initial reduction stages is controlled by the combined gaseous diffusion and interfacial chemical reaction mechanisms while at the final reduction stages the reaction is controlled by the interfacial chemical reaction mechanism.

収録刊行物

  • Materials transactions  

    Materials transactions 49(2), 352-359, 2008-02-01 

    The Japan Institute of Metals and Materials

参考文献:  26件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10021144308
  • NII書誌ID(NCID)
    AA1151294X
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    13459678
  • NDL 記事登録ID
    9354681
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z53-J286
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ