Low-Pressure Infiltration Behavior of Molten Metal to Porous FeCrSi Preform
Porous preform reinforced aluminum alloy composite were prepared by the infiltration of molten metal using a low-pressure casting. The infiltration behavior of the filling pattern and the velocity profile obtained for alloys fabricated by the low-pressure casting process was investigated. The infiltration times in the case where a barrier palate was placed on the preform and at the pressure acceleration times of 1, 2 and 5 s were experimentally investigated under a constant applied pressure of 0.4 MPa. The infiltration at the pressure acceleration time of 1, 2 and 5 s ended in 5.36, 5.8 and 6.2 s, respectively. Hence, the infiltration time was short if the pressure acceleration time was short.
- Materials transactions
Materials transactions 49(2), 390-392, 2008-02-01
The Japan Institute of Metals and Materials