Phase Constituents and Compressive Yield Stress of Ni-Co Base Alloys
-
- Cui C. Y.
- High Temperature Materials Center, National Institute for Materials Science
-
- Gu Y. F.
- High Temperature Materials Center, National Institute for Materials Science
-
- Ping D. H.
- High Temperature Materials Center, National Institute for Materials Science
-
- Fukuda T.
- High Temperature Materials Center, National Institute for Materials Science
-
- Harada H.
- High Temperature Materials Center, National Institute for Materials Science
Search this article
Abstract
Phase constituents and compressive yield stress of Ni-Co base alloys have been investigated. The results showed that two-phases of γ and γ′ were the main constituents in all the alloys. Ni3Ti-type (η) phase was observed in the alloys with lower Co and Ti content (alloy20); while a new intermetallic (Ni,Co,Cr)3(Ti,Al) phase with a hexagonal structure was detected in the higher Co and Ti containing alloy(alloy50). At temperatures lower than 1023 K, the compressive yield stress increased with increasing Co content up to 28.6 mass% and Ti content up to 7.4 mass%, but decreased with more Co and Ti addition. At temperatures higher than 1273 K, all the alloys showed similar yield stress.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (3), 424-427, 2008
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204249628672
-
- NII Article ID
- 10021144524
- 130004453924
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 9412849
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed