Glass Forming Ability and Mechanical Properties of New Ni-Based Bulk Metallic Glasses

• Li Song

  Institute for Materials Research, Tohoku University

• Xie Guoqiang

  Institute for Materials Research, Tohoku University

• Louzguine-Luzgin Dmitri V.

  Institute for Materials Research, Tohoku University

• Inoue Akihisa

  Institute for Materials Research, Tohoku University

抄録

New Ni-Zr-Cu-Ti-Al bulk metallic glasses (BMGs) were fabricated on the basis of ternary Ni-Zr-Al alloys. The addition of Cu and Ti increased the glass-forming ability (GFA) of Ni-Zr-Al alloys. These BMGs exhibited high thermal stability and relatively large supercooled-liquid region. With the substitution of Ni by Cu from 0 to 19.2 at%, the GFA of Ni-Zr-Ti-Al alloys was enhanced and its glass transition temperature T_g, onset crystallization temperature T_x, and onset melting temperature T_m all decreased. When Cu content was 24 at%, the GFA decreased again. The BMG rod with a maximum diameter of 2 mm was fabricated in the Ni_43.7Zr_19.2Cu_19.2Ti_13.9Al₄ alloy and the compression tests indicated that it had high fracture strength of about 2400 MPa, Young’s modulus of 121 GPa, elastic strain of 0.02 and plastic strain of 0.009 at ambient temperature.

収録刊行物

• MATERIALS TRANSACTIONS

  MATERIALS TRANSACTIONS 49 (3), 494-497, 2008

  公益社団法人 日本金属学会

キーワード

• bulk metallic glass
• glass-forming ability
• mechanical properties

詳細情報

• CRID: 1390282679226361984
• NII論文ID: 10021144805
• NII論文ID: 130004453934
• NII書誌ID: AA1151294X
• DOI: 10.2320/matertrans.mbw200728
• ISSN: 13475320
• ISSN: 13459678
• NDL書誌ID: 9412983
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I9412983
• Web Site: https://www.jstage.jst.go.jp/article/matertrans/49/3/49_MBW200728/_pdf
• 本文言語コード: en
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可