Excellent Thermal Stability and Bulk Glass Forming Ability of Fe-B-Nb-Y Soft Magnetic Metallic Glass
-
- Lee Sangmin
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Kato Hidemi
- Institute for Materials Research, Tohoku University
-
- Kubota Takeshi
- Institute for Materials Research, Tohoku University
-
- Yubuta Kunio
- Institute for Materials Research, Tohoku University
-
- Makino Akihiro
- Institute for Materials Research, Tohoku University
-
- Inoue Akihisa
- Tohoku University
この論文をさがす
抄録
Effects of Y addition on the glass forming ability (GFA) of a Fe-B-Nb marginal glass former, and annealing effects on glassy/supercooled liquid phases as well as soft magnetic properties in the multicomponent Fe-B-Nb-Y alloy system were investigated. The origin of highly improved GFA in the multicomponent system is discussed with related to a characteristic exothermic phase transformation, chemical short range ordering, in the supercooled liquid region due to the positive heat of mixing between Nb-Y elements. The separating tendency between Nb and Y elements is considered to suppress precipitation of metastable Fe23B6 and α-Fe crystalline phases, thus to result in highly improving GFA and distinct high thermal stability against heat treatment of the alloy system. In addition, a glassy ring was fabricated by copper mold casting and magnetic properties were investigated before/after heat treatment.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (3), 506-512, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204249678080
-
- NII論文ID
- 10021144873
- 130004453936
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- HANDLE
- 10097/52321
-
- NDL書誌ID
- 9413012
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可