- Tu Meng-Yin
- Department of Materials Science and Engineering, National Taiwan University
-
- Wang Wen-Hsiung
- Department of Materials Science and Engineering, National Taiwan University
-
- Hsu Yung-Fu
- Department of Materials and Mineral Resources Engineering, National Taipei University of Technology
この論文をさがす
抄録
This study investigates the relationship between the morphology and the fracture behavior of upper bainite in JIS SK5 steel. The cleavage crack path was found to lie on {001}α, {112}α or {123}α using electron backscatter diffraction (EBSD) from the fracture surface. Additionally, most of the bainite sheaf boundaries were found to be high-angle boundaries. If the cleavage planes are presumed to lie uniquely on {001}α, then most of the deviations of the angles between two K-S variants in a given austenite grain are high-angle deviations. According to TEM diffraction analysis, the orientation relationship of cementite/bainitic ferrite satisfies the Bagaryatskii relation, and the habit plane of cementite precipitated in the bainite sheaf locates on (0\\bar11)α||(100)θ. Cementite does not significantly affect the propagation of a cleavage crack. Hence, cleavage cracking deflects at grain boundaries or bainite sheaf boundaries, but only reinitiates at the cementite/bainitic ferrite interface.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (3), 559-564, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679226374400
-
- NII論文ID
- 10021145068
- 130004453943
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9413116
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可