抄録
The heat treatment parameters of AZ64 magnesium alloy have been optimized using thermal analysis, scanning electron microscopy and X-ray diffraction techniques. The thermal analysis result revealed that two precipitation reactions took place during the solidification of AZ64 alloy. Therefore, a two-step solution heat treatment method, instead of traditional solution treatment whose temperature was about 10°C below the solidus temperature, was developed corresponding to the dissolution of two precipitate phases. With comparison to the traditional heat treatment, the two-step treatment method could generate a complete solution effect. During the following aging process, precipitates almost uniformly dispersed throughout the matrix, thus improve the tensile strength of alloy.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (5), 986-989, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679226151936
-
- NII論文ID
- 10021146555
- 130004453977
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9480362
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可