Effects of Nb on the Microstructure and Elevated-Temperature Mechanical Properties of Alloy 690-SUS 304L Dissimilar Welds

この論文にアクセスする

この論文をさがす

著者

抄録

The purpose of this paper was to investigate the effects of Nb on the microstructure and elevated-temperature mechanical properties of Alloy 690-SUS 304L dissimilar welds. The results show that the welds were dominant with dendrites and interdendritic phases. In the low Nb welds, the main interdendritic phases were Nb-rich and Al-Ti-rich phases. Cr-carbides were precipitated along the grain boundaries of the root region. In the high Nb welds, there were large Nb-rich phases in the cap region, while smaller Nb-carbonitride precipitates were found in the root region. The addition of Nb increased the hardness of the fusion zones. At 300°C, though the tensile strengths of all welds were higher than that of 304L, micro-cracks were unexpectedly found in the low Nb weld. Notched specimens were tested to characterize the mechanical properties of the welds. Both of the yielding and tensile strengths of the welds increased with Nb additions. On the fracture surface, the brittle fracture features also became noticeable.

収録刊行物

  • Materials transactions  

    Materials transactions 49(6), 1270-1277, 2008-06-01 

    The Japan Institute of Metals and Materials

参考文献:  16件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10021147345
  • NII書誌ID(NCID)
    AA1151294X
  • 本文言語コード
    ENG
  • 資料種別
    ART
  • ISSN
    13459678
  • NDL 記事登録ID
    9519105
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z53-J286
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ