Nucleation of the primary Al phase on TiAl3 during solidification in hot-dip Zn-11%Al-3%Mg-0.2%Si-coated steel sheet
-
- Honda Kazuhiko
- Kimitsu R&D Lab, Technical Development Bureau, Nippon Steel Corp.
-
- Ushioda Kohsaku
- Kimitsu R&D Lab, Technical Development Bureau, Nippon Steel Corp.
-
- Yamada Wataru
- Kimitsu R&D Lab, Technical Development Bureau, Nippon Steel Corp.
-
- Tanaka Koki
- Advanced Technology Research Lab, Technical Development Bureau, Nippon Steel Corp.
-
- Hatanaka Hidetoshi
- Kimitsu Works, Nippon Steel Corp.
書誌事項
- タイトル別名
-
- Nucleation of the Primary Al Phase on TiAl<SUB>3</SUB> during Solidification in Hot-Dip Zn-11%Al-3%Mg-0.2%Si-Coated Steel Sheet
この論文をさがす
抄録
The solidification structure of a hot-dip Zn-11%Al-3%Mg-0.2%Si coated steel sheet with a slight Ti addition was investigated by EBSD. In every center of the primary Al phase of the alloy-coating layer, TiAl3 was observed by a scanning electron microscope, which suggests that TiAl3 acts as a heterogeneous nucleation site of the primary Al phase. The latter was revealed to have perfect lattice coherency with the nucleus TiAl3 phase. The crystal orientation relationships between TiAl3 and the primary Al are (001)TiAl<SUB>3</SUB>||(001)Al and [100]TiAl<SUB>3</SUB>||[100]Al, (100)TiAl<SUB>3</SUB>||(001)Al and [001]TiAl<SUB>3</SUB>||[100]Al, (102)TiAl<SUB>3</SUB>||(110)Al and [\\bar201]TiAl<SUB>3</SUB>||[\\bar110]Al, (110)TiAl<SUB>3</SUB>||(110)Al and [\\bar110]TiAl<SUB>3</SUB>||[\\bar110]Al, indicating that the primary Al phase grows in an epitaxial manner from the nucleus TiAl3 phase. The planar disregistry δ between the two phases was calculated to be less than 5%, owing to this good lattice coherency. The TiAl3 phase is considered to decrease the degree of undercooling necessary for the nucleation of the primary Al phase.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (6), 1401-1409, 2008
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679226118528
-
- NII論文ID
- 10021147710
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9519470
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可