Improvement of Glass Forming Ability of Cu-Ni-Zr-Ti Alloys by Substitution of Hf and Nb
-
- Lee Dong-Myoung
- Department of Metallurgical Engineering, Inha University Advanced Functional Material Team, Korea Institute of Industrial Technology
-
- Sun Ju-Hyun
- Advanced Functional Material Team, Korea Institute of Industrial Technology
-
- Shin Seung-Yong
- Advanced Functional Material Team, Korea Institute of Industrial Technology
-
- Bae Jeong-Chan
- Advanced Functional Material Team, Korea Institute of Industrial Technology
-
- Lee Chi-Hwan
- Department of Metallurgical Engineering, Inha University
この論文をさがす
抄録
New bulk metallic glasses exhibiting a high glass forming ability were formed by a substitution of Hf and Nb for Zr and Ti in quaternary Cu-Ni-Zr-Ti system. An 8 mm-diameter BMG rod was obtained at the Cu50Ni8Zr15Hf3Ti23Nb1 composition by suction casting method. The glass transition temperature, crystallization temperature and reduced glass transition temperature of the BMG were 699 K, 754 K, and 0.59, respectively. Making an alloy system more complex was useful to increase the GFA.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (6), 1486-1489, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679226097536
-
- NII論文ID
- 10021147979
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9519654
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可