Effect of Milling on the Carbothermal Reduction of Oxide Mixture for (Ti,W)C-Ni
-
- Kwon Hanjung
- Department of Materials Science and Engineering, Seoul National University
-
- Kang Shinhoo
- Department of Materials Science and Engineering, Seoul National University
この論文をさがす
抄録
The effect of high-energy milling on the phase transformation and carbothermal reduction was examined using an oxide mixture, TiO2-WO3-NiO-C, with a process to synthesize (Ti,W)C cermets. Due to the high energy involved in the mill raw, anatase TiO2 transformed first to TiO2-II and then to rutile, while WO3 transformed to a high-pressure WO3-HP and hexagonal WO3 phase. The co-existence of WO3 and TiO2 enhanced the formation of a nano-crystalline or amorphous phase. The (Ti,W)C phase was formed mainly at 1150°C from TiC and WC formed in the early stages. These results were further examined using XRD, the Rietveld method and mass spectroscopy.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (7), 1594-1599, 2008
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204248908032
-
- NII論文ID
- 10021148297
- 130004454021
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 9555658
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可