Re-Cr-Ni系における1423Kの等温状態図の実験的決定 Experimental Determination of Isothermal Phase Diagram at 1423K in the Ternary Re-Cr-Ni System

この論文にアクセスする

この論文をさがす

著者

抄録

  Compositions with tie-lines between the γ, α, σ, and δ phases in a ternary Re-Cr-Ni system were investigated by heat-treating various ternary Re-Cr-Ni alloys in vacuum at 1423 K for a variety of heating times up to 2500 h. The microstructures of the Re-Cr-Ni alloys that had been water-quenched after heating were observed and their Re, Cr and Ni concentration profiles were measured using an electron probe micro-analyzer (EPMA). It was found that a very long heat treatment was required to obtain equilibrium compositions of Ar-arc-melted Re-Cr-Ni alloys.<br>    The tie-line compositions (at%) of each phase at 1423 K were experimentally determined, and an isothermal phase diagram was constructed. From these results, the γ, α, and σ phases of the three-phase coexistence state were found to have the following compositions: γ phase (3.0 at%Re, 45.6 at%Cr, and 51.4 at%Ni), α phase (16.1 at%Re, 75.2 at%Cr, and 8.7 at%Ni), and σ phase (16.3 at%Re, 60.3 at%Cr, and 23.4 at%Ni). In addition, the γ, σ, and δ phases have the following compositions: γ phase (13.3 at%Re, 18.1 at%Cr, and 68.6 at%Ni), σ phase (54.6 at%Re, 24.2 at%Cr, and 21.2 at%Ni), and δ phase (70.2 at%Re, 6.0 at%Cr, and 23.8 at%Ni).<br>    The solubility limits of Ni in the σ phase increased from 19 at%Ni to 24 at%Ni, as the Cr content in the σ phase with a tie-line with the γ phase increased from 23 at%Cr to 61 at%Cr.<br>

収録刊行物

  • 日本金屬學會誌 = Journal of the Japan Institute of Metals  

    日本金屬學會誌 = Journal of the Japan Institute of Metals 72(2), 132-137, 2008-02-01 

    The Japan Institute of Metals

参考文献:  16件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  2件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10021149740
  • NII書誌ID(NCID)
    AN00062446
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    00214876
  • NDL 記事登録ID
    9371354
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-314
  • データ提供元
    CJP書誌  CJP引用  NDL  J-STAGE 
ページトップへ