鉄鋼圧延ロール用多合金系白鋳鉄の圧縮特性に及ぼす化学組成の影響 Effects of Chemical Composition on Compressive Properties of Multicomponent White Cast Irons for Steel Rolling Mill Roll

この論文にアクセスする

この論文をさがす

著者

抄録

  Multi-component white cast irons containing Cr, Mo, W and V are widely popular as roll materials for hot strip finishing mills because of their excellent wear resistance. Work rolls of multiple rolling mills applied usually to hot strip finish rolling are required to endure the contact pressure generated by rolling force between work roll and back-up roll or intermediate roll. In this research, effects of alloy and C contents on compressive properties were investigated. 0.2% compressive proof strength was found to increase with increase in hardness. It was also found that the relation is σ<sub>0.2</sub> (MPa)=3.52・HV30-588 for irons with martensitic and fine pearlitic matrices. The equation <i>P</i><sub>max</sub>=1.65・σ<sub>0.2%</sub> was obtained between Hertzian contact pressure and compressive proof strength. In order for rolls to endure contact pressure of 2.6GPa, compressive proof strength over 1.6GPa is necessary and multi-component white cast irons with macro-hardness over 600HV30 can be said to be appropriate roll materials for recent hot strip finishing mills applied by heavy load.

収録刊行物

  • 鋳造工学 = Journal of Japan Foundry Engineering Society  

    鋳造工学 = Journal of Japan Foundry Engineering Society 80(5), 272-277, 2008-05-25 

    Japan Foundry Engineering Society

参考文献:  9件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10021162113
  • NII書誌ID(NCID)
    AN10514770
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    13420429
  • NDL 記事登録ID
    9512173
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-277
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ