マグネシウム合金溶湯に対するVGCFのぬれ性改善を目的とした表面改質処理 On the Surface Modification for Wettability of the VGCF to Molten Magnesium Alloy

この論文にアクセスする

この論文をさがす

著者

抄録

Si was sublimated at 1400 degrees in a vacuum, and caused to react with the VGCF. Based on the mixed rate of Si, it became clear that sublimated Si reacts to the VGCF surface partially or fully, and forms the reaction phase of SiC. As a result of evaluating wettability, it became clear that SiC phase causes the molten magnesium alloy to have good wettability.

収録刊行物

  • 表面技術 = The Journal of the Surface Finishing Society of Japan

    表面技術 = The Journal of the Surface Finishing Society of Japan 59(4), 265-267, 2008-04-01

    The Surface Finishing Society of Japan

参考文献:  6件中 1-6件 を表示

  • <no title>

    WANG Y. H.

    Nanotechnology 17, 3817, 2006

    被引用文献1件

  • <no title>

    MORISADA Y.

    Materials Integration 17, 39, 2004

    被引用文献1件

  • <no title>

    OBERLIN A.

    Journal of Crystal Growth 32, 335-349, 1976

    DOI 被引用文献35件

  • <no title>

    IIJIMA S.

    Nature 363, 603-605, 1993

    DOI 被引用文献112件

  • <no title>

    FEITH S.

    J. adhes. sci. technol 12, 523, 1998

    被引用文献1件

  • <no title>

    XU Y.

    Cement and Concrete Research 29, 773, 1999

    被引用文献1件

各種コード

  • NII論文ID(NAID)
    10021169798
  • NII書誌ID(NCID)
    AN1005202X
  • 本文言語コード
    JPN
  • 資料種別
    NOT
  • ISSN
    09151869
  • NDL 記事登録ID
    9455048
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-291
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ