ブラスト処理を施したTi-6Al-4V合金基板へのリン酸カルシウムコーティングと生体内外評価 Fabrication and Evaluation of Calcium Phosphate Coating Films on Blast-treated Ti-6Al-4V Alloy Substrate

この論文にアクセスする

この論文をさがす

著者

抄録

Calcium phosphate coating films were fabricated on Ti-6Al-4V alloy plates and implants with a blast-treated surface using radiofrequency (RF) magnetron sputtering and were evaluated <I>in vitro</I> and <I>in vivo</I>. Amorphous calcium phosphate (ACP) and oxyapatite (OAp) films obtained in this study could cover the blast-treated Ti-6Al-4V substrate very efficiently, maintaining the surface roughness. For the in vitro evaluations of the calcium phosphate coating films, bonding strength and alkaline phosphatase (ALP) activity were examined. The bonding strength of the coating films to a blast-treated Ti-6Al-4V plate exceeded 60 MPa, independent of film phases. When compared with an uncoated Ti-6Al-4V plate, the increase in the ALP activity of osteoblastic SaOS-2 cells on a blast-treated Ti-6Al-4V plate coated with the ACP and OAp films was confirmed by a cell culture test. The removal torque of screw type Ti-6Al-4V implants with a blast-treated surface from the femur of a Japanese white rabbit increased with the duration of implantation and it was statistically improved by coating an ACP film two weeks after implantation. The <I>in vitro</I> and <I>vivo</I> studies suggested that the application of the sputtered ACP film as a coating on titanium implants was effective in improving their biocompatibility with the bones.

収録刊行物

  • 粉体および粉末冶金  

    粉体および粉末冶金 55(5), 318-324, 2008-05-15 

    Japan Society of Powder and Powder Metallurgy

参考文献:  19件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

各種コード

  • NII論文ID(NAID)
    10021173134
  • NII書誌ID(NCID)
    AN00222724
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    05328799
  • NDL 記事登録ID
    9531490
  • NDL 雑誌分類
    ZP41(科学技術--金属工学・鉱山工学)
  • NDL 請求記号
    Z17-274
  • データ提供元
    CJP書誌  NDL  J-STAGE 
ページトップへ