<原著>試作α-リン酸三カルシウム/リン酸四カルシウム系セメントの物理化学的性質 <ORIGINAL ARTICLE>Physico-chemical Properties of a New α-Tricalcium Phosphate/Tetracalcium Phosphate Cements

この論文にアクセスする

この論文をさがす

著者

    • 足立 正徳 ADACHI MASANORI
    • 朝日大学歯学部歯科理工学講座 Department of Dental Materials and Technology, School of Dentistry, Asahi University
    • 後藤 隆泰 GOTO TAKAYASU
    • 朝日大学歯学部歯科理工学講座 Department of Dental Materials and Technology, School of Dentistry, Asahi University
    • 亀水 秀男 KAMEMIZU HIDEO
    • 朝日大学歯学部歯科理工学講座 Department of Dental Materials and Technology, School of Dentistry, Asahi University
    • 飯島 まゆみ IIJIMA MAYUMI
    • 朝日大学歯学部歯科理工学講座 Department of Dental Materials and Technology, School of Dentistry, Asahi University
    • 金 昇孝 KIM S. -H.
    • 朝日大学歯学部歯科理工学講座 Department of Dental Materials and Technology, School of Dentistry, Asahi University
    • 土井 豊 DOI YUTAKA
    • 朝日大学歯学部歯科理工学講座 Department of Dental Materials and Technology, School of Dentistry, Asahi University

抄録

リン酸三カルシウム(α-TCP)とリン酸四カルシウム(TeCP)がモル比(α-TCP/TeCP)で2/3, 2/1, 6/1の3種類のα-TCP・TeCP系セメントを乾式合成し,20wt%リン酸二水素ナトリウム(NaH_2P0_4)水溶液および20wt%NaH_2P0_4・20wt%DL-リンゴ酸水溶液で練和した硬化体の物理化学的性質を検討した.その結果,いずれのセメント粉末でも20wt%NaH_2P0_4・20wt%DL-リンゴ酸水溶液の場合のみ硬化し,粉液比が1.8(粉g/液ml)で硬化時間は約3分となった.硬化時のpHはいずれの組み合わせでも中性から弱アルカリ性を示した.また,硬化体の間接引張強度は蒸留水浸潰7日後まで徐々に増加し,20wt%NaH_2P0_4・20wt%DL-リンゴ酸水溶液で練和したα-TCP/TeCP=2/1セメントでは最大約5MPaに達した.さらに蒸留水中における硬化時の寸法変化はいずれの場合も5時間後で約0.5%と僅かな収縮を示した.

In this study, cements consisting of α-tricalcium phosphate (α-TCP) and tetracalcium phosphate (TeCP) at various molar ratios (α-TCP/TeCP) of 2/3, 2/1 and 6/1 were directly synthesized from raw materials of CaCO_3 and CaHPO_4・2H_2O by heating them at 1500°C for 5 hrs, and the physico-chemical properties of cements mixed with two types of liquid at a powder-liquid ratio of 1.8 (powder g/liquid ml) were examined. The cements mixed with 20 wt% NaH_2PO_4 solution required a extremely long time to set, whereas the setting time of the cements mixed with 20 wt% NaH_2PO_4 and 20 wt% DL-malic acid solution were about three minutes, regardless of the difference in α-TCP/TeCP ratio of the cements. The pH of setting cement varied from neutral to weekly alkaline in every combination of powder and liquid. The diametral tensile strengths of all cements immersed in distilled water increased gradually with time, and reached 5 MPa for the ct-TCP/TeCP=2/1 cement mixed with 20 wt% NaH_2PO_4・20 wt% DL-malic acid solution. The resilts of these physico-chemical tests suggested that the present cement powder synthesized by a new method was applicable to endodontic treatment as a root canal filling agent or a pulp capping agent in dentistry.

収録刊行物

参考文献:  37件

参考文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。

被引用文献:  1件

被引用文献を見るにはログインが必要です。ユーザIDをお持ちでない方は新規登録してください。