チタンにコーティングしたアルミナ薄膜に対する<i>Porphyromonas gingivalis</i> の初期付着特性

• 五十嵐 崇恭

  (社)日本歯科先端技術研究所

• 広瀬 大希

  (社)日本歯科先端技術研究所

• 金子 守男

  (社)日本歯科先端技術研究所

• 五十嵐 俊男

  (社)日本歯科先端技術研究所 神奈川歯科大学顎顔面外科学講座 東京歯科大学口腔科学研究センター口腔インプラント学研究部門

• 吉成 正雄

  東京歯科大学口腔科学研究センター口腔インプラント学研究部門

書誌事項

タイトル別名

• Initial Adhesion of <i>Porphyromonas gingivalis</i> on Thin Alumina-coated Titanium

抄録

This study was designed to evaluate the initial adherence (during the first hour) of Porphyromonas gingivalis (P.g.) as well as the surface characterization of alumina-coated titanium using a physical vapor deposition technique in order to reduce the adherence of bacteria to titanium implants. The coatings were defect-free films approximately 2 μm thick that were strongly adhered to the titanium substrate and were identified as αalumina. The contact angle to water was 63 degrees (SD: 5 degrees), which was almost equal to that of titanium. The zeta potential at pH 7.0 was 22.4 mV (SD: 3.2 mV), indicating positively charged at around pH 7. The amount of initial adhesion of P.g. was remarkably decreased on alumina-coated surfaces compared to polished titanium. The adherence of P.g. was considered to be related to the surface electrical charge of the materials.These results suggested that a thin alumina coating on titanium is a promising method for reducing the initial adhesion of oral bacteria.

収録刊行物

• 日本口腔インプラント学会誌

  日本口腔インプラント学会誌 21 (2), 311-318, 2008

  公益社団法人 日本口腔インプラント学会

キーワード

• alumina
• thin coating
• surface characterization
• bacterial adhesion

詳細情報

• CRID: 1390282680485691776
• NII論文ID: 130003398211
• NII論文ID: 10021952721
• NII書誌ID: AN10072606
• DOI: 10.11237/jsoi.21.311
• ISSN: 21879117
• ISSN: 09146695
• Web Site: https://search.jamas.or.jp/link/ui/2008316485
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • CiNii Articles
  • KAKEN
• 抄録ライセンスフラグ: 使用不可