- Effect of n value and dislocation structures on the elongation of aluminum alloy sheets
- アルミニウム ゴウキンバン ノ ノビ ニ オヨボス nチ ト テンイ ソシキ ノ エイキョウ
この論文をさがす
抄録
The effects of the n value and dislocation structures on the elongation of aluminum alloy sheets were investigated. The n value of the aluminum alloy was not constant. It increased to the maximum n value and decreased with strain. When the n value was constant, dislocation cell structures were observed. When the n value decreased, microbands were observed. It was considered that an increasing n value denoted an increasing dislocation density and a decreasing n value denoted a dynamic recovery occurring such as the formation of microbands. The decreasing rate after the maximum n value was a more important parameter than the average or the maximum n value for the relationship with the elongation. The Al–Mg–Si alloys and the Al-low Mg alloys had a highly decreasing n value rates. The pure aluminum and Al-high Mg alloys had low decreasing n value rates. It was considered that the highly decreasing rate after the maximum n value suggested a dynamic recovery and easily occurring local necking.
収録刊行物
-
- 軽金属
-
軽金属 58 (7), 290-294, 2008
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681317342464
-
- NII論文ID
- 10021989373
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DC%2BD1cXhtVCiur3F
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 9602376
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可