ソーダライムガラスの微小な破壊抵抗に及ぼす電子線照射の効果

• 岩田 圭祐

  東海大学大学院理工学研究科総合理工学専攻

• 西 義武

  東海大学大学院理工学研究科総合理工学専攻

書誌事項

タイトル別名

• Effects of Electron Beam Irradiation on Microscopic Fracture Resistance of Soda Lime Glass
• ソーダ ライム ガラス ノ ビショウナ ハカイ テイコウ ニ オヨボス デンシセン ショウシャ ノ コウカ

抄録

  An effect of electron beam (EB) irradiation on the fracture resistance of soda lime glass was studied. EB-irradiation with small dose less than 1 MGy and low potential less than 170 keV could not change the plastic deformation energy to propagate the crack (E_f^p), which was estimated by fracture toughness (K_IC) using standard indentation fracture method. On the other hand, EB irradiation of less than 0.43 MGy increased the plastic deformation energy to generate the crack (E_f). If EB-irradiation annihilated the spontaneous crack origins, it could be explained the increasing E_f value. In addition, if EB-irradiation formed dangling bonds in glassy network structure, they probably relaxed the residual stress and should prevent the crack generation. As the result of electron spin resonance spectra showed, the EB irradiation generated dangling bonds in the soda lime glass and partial relaxation of the residual strain mainly occurred around these dangling bonds of the weakly bonded metal (Na and Mg)-oxygen pairs in the network structure. The increased crack generation energy was therefore mainly due to the relaxation of the strongly bonded metal-oxygen atomic pairs in the network structure, as well as the annihilation of crack origin.<br>

収録刊行物

• 日本金属学会誌

  日本金属学会誌 73 (1), 46-51, 2009

  公益社団法人 日本金属学会

キーワード

• electron beam irradiation
• fracture resistance
• soda lime glass
• dangling bond

詳細情報

• CRID: 1390001206479061120
• NII論文ID: 10024817718
• NII書誌ID: AN00187860
• DOI: 10.2320/jinstmet.73.46
• ISSN: 18806880
• ISSN: 24337501
• ISSN: 00214876
• NDL書誌ID: 9769243
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I9769243
• Web Site: https://www.jstage.jst.go.jp/article/jinstmet/73/1/73_1_46/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
  • KAKEN
• 抄録ライセンスフラグ: 使用不可