Selective sorption of Co[2+] over Ni[2+] using biogenic manganese oxides
-
- Sasaki Keiko
- Department of Earth Resources Engineering, Kyushu University
-
- Kaseyama Takuya
- Department of Earth Resources Engineering, Kyushu University
-
- Hirajima Tsuyoshi
- Department of Earth Resources Engineering, Kyushu University
書誌事項
- タイトル別名
-
- Selective Sorption of Co<SUP>2+</SUP> over Ni<SUP>2+</SUP> Using Biogenic Manganese Oxides
- Selective sorption of Co(II) over Ni(II) using biogenic manganese oxides
この論文をさがす
抄録
Preferential sorption of Co2+ ions over Ni2+ ions was achieved using biogenic Mn oxides produced by the Mn-oxidizing fungus Paraconiothyrium sp. WL-2 strain with a maximum selectivity coefficient (αCo) of 18. The selective sorption was based on different sorption mechanism for Co2+ and Ni2+ and unique properties of biogenic Mn oxides. The octahedral Co2+ ions occupy vacancies of central metal sites and edge sites in the octahedral Mn oxide unit structures of biogenic Mn oxides, where they are immobilized by oxidation to CoOOH by Mn(III). In contrast, Ni2+ ions are sorbed primarily on layer edges at circumneutral pHs without oxidation. Selective sorption of Co2+ over Ni2+ on the biogenic Mn oxides results from more vacant sites, higher Mn(III) contents, and larger specific surface areas compared to synthetic Mn oxides.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 50 (11), 2643-2648, 2009
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679225997440
-
- NII論文ID
- 10025559179
- 130004454147
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10417941
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可