Effect of CaO and ZrO2 co-substitution on dielectric properties of BaTi2O5 prepared by arc melting
-
- YUE Xinyan
- Key Laboratory for Anisotropy and Texture of Materials (MOE), School of Materials and Metallurgy, Northeastern University
-
- TU Rong
- Institute for Materials Research, Tohoku University
-
- GOTO Takashi
- Institute for Materials Research, Tohoku University
-
- RU Hongqiang
- Key Laboratory for Anisotropy and Texture of Materials (MOE), School of Materials and Metallurgy, Northeastern University
この論文をさがす
抄録
CaO and ZrO2 co-substituted polycrystalline BaTi2O5, (Ba1-xCax)(Ti0.995Zr0.005)2O5, (BCT2Z), was prepared by arc melting and the dielectric properties were investigated by AC impedance spectroscopy. b-direction orientation was obtained at any composition. The lattice parameters of a-, b- and c-axes first increased until x = 0.003 and then slightly decreased with increasing CaO content up to x = 0.020. The maximum permittivity of polycrystalline BaTi2O5 showed the highest value of 6230 at x = 0.020. The Tc of polycrystalline BaTi2O5 slightly decreased from 750 to 716 K when CaO content was increased up to 0.020.
収録刊行物
-
- Journal of the Ceramic Society of Japan
-
Journal of the Ceramic Society of Japan 117 (1364), 435-438, 2009
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205283129344
-
- NII論文ID
- 10025966933
-
- NII書誌ID
- AA12229489
-
- ISSN
- 13486535
- 18820743
-
- HANDLE
- 10097/52384
-
- NDL書誌ID
- 10198286
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可