Vertical and horizontal directional solidification of Zn-Al and Zn-eg diluted alloys
-
- Gueijman Sergio F.
- School of Science, National University of Misiones
-
- Schvezov Carlos E.
- School of Science, National University of Misiones National Science Research Council of Argentina (CONICET)
-
- Ares Alicia E.
- School of Science, National University of Misiones National Science Research Council of Argentina (CONICET)
書誌事項
- タイトル別名
-
- Vertical and Horizontal Directional Solidification of Zn-Al and Zn-Ag Diluted Alloys
この論文をさがす
抄録
Zinc-Aluminum and Zinc-Silver alloys were solidified in horizontal and vertical form and the results obtained analyzed. Thermal parameters such as the cooling rates, the liquidus and solidus interphase velocities, and the temperature gradients were determined. The velocity of the liquidus interphase is greater than or sometimes equal to the velocity of the solidus interphase. In the vertical setup, columnar-to-equiaxed (CET) grain transition was obtained. CET does not occur in the horizontal one-directional solidification when critical minimum gradients reach values greater than 0.1 K/mm.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 51 (10), 1861-1870, 2010
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報
-
- CRID
- 1390001204250025088
-
- NII論文ID
- 10026695441
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10831690
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可