• Magnetoresistance Effect of Granular Films Employing Co2FeAl0.5Si0.5 Alloy
• Co2FeAl0 5Si0 5 ゴウキン オ モチイタ グラニュラー ハクマク ノ ジキ テイコウ コウカ

抄録

Magnetoresistance (MR) effects and electroric structure were investigated for granular films employing Co₂FeAl_0.5Si_0.5 (CFAS) alloy. CFAS-MgO granular films showed a maximum MR ratio of approximately 4.8 %. It was however recognized that the surface of CFAS granules was slightly oxidized due to the low formation energy of MgO matrix. By utilizing MgF₂ matrix, the MR ratio increased to approximately 6.5 %. After annealing at 200°C, the MR ratio increased slightly. It was thought that the L2₁ ordered structure was not obtained due to the low annealing temperature. Further annealing at high temperature is required to obtain L2₁ ordered CFAS granules.

収録刊行物

• 電気学会論文誌．　Ａ

  電気学会論文誌．　Ａ 130 (7), 626-630, 2010

  一般社団法人 電気学会

キーワード

• グラニュラー薄膜
• トンネル磁気抵抗
• ハーフメタル

詳細情報

• CRID: 1390001204599420416
• NII論文ID: 10026865145
• NII書誌ID: AN10136312
• DOI: 10.1541/ieejfms.130.626
• ISSN: 13475533
• ISSN: 03854205
• NDL書誌ID: 10740727
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I10740727
• Web Site: http://www.jstage.jst.go.jp/article/ieejfms/130/7/130_7_626/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可