- Tantalum Recovery from Printed Circuit Board by Heat Treatment
- ネツ ショリ ニ ヨル プリント キバン カラ ノ タンタル カイシュウ
この論文をさがす
抄録
In an attempt to recover tantalum from Printed Circuit board (PCB) , tantalum was concentrated by heat treatment and physical separation from mounted parts for PCB. Tantalum of PCBs is derived from tantalum capacitors. PCBs for personal computer (PC) and household appliance were crushed by water explosion to strip mounted parts from PCBs. More parts were stripped from PCB for PC composed of epoxy resin than from PCB for household appliance composed of phenol resin. Then, tantalum sintered bodies were separated from molded resins by heat treatment for tantalum capacitors at 723, 773K in the air and screening with 0.5mm sieve. 70% of tantalum grade was obtained after separation for tantalum capacitors. Tantalum recovery decreased under the condition of heat treatment at low oxygen concentration. Behavior of other parts by heat treatment was also investigated. While epoxy resin molding IC parts was powderized at over 723K, tantalum sintered body was powderized at over 823K. As a result, mounted parts of PCB for hard disk drive (HDD) were heated at 723K and the residue with size over 0.5mm was re-heated at 823K and screened. Material balances of tantalum, copper and precious metals were investigated on the process. 16% of tantalum grade and 71% of tantalum recovery was obtained. 13% of copper, 49% of gold, 12% of silver and 16% of palladium were distributed to the tantalum concentrated residue.
収録刊行物
-
- 資源と素材
-
資源と素材 127 (8), 519-525, 2011
一般社団法人 資源・素材学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205280791808
-
- NII論文ID
- 10029260206
-
- NII書誌ID
- AA12188381
-
- COI
- 1:CAS:528:DC%2BC3MXhtlWqs7vE
-
- ISSN
- 18840450
- 18816118
-
- NDL書誌ID
- 11199321
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可