- Effect of pre-aging conditions on T5 heat treatment behavior of Al-9%Si-0.3%Mg die-casting alloy
- Al-9%Si-0.3%Mgダイカスト合金のT5熱処理挙動における予備時効条件の影響
- Al 9% Si 0 3% Mg ダイカスト ゴウキン ノ T5 ネツ ショリ キョドウ ニ オケル ヨビ ジコウ ジョウケン ノ エイキョウ
この論文をさがす
抄録
Effect of pre-aging conditions on T5 heat treatment behavior of Al–9.0%Si–0.3%Mg die-casting alloy was investigated by using hardness measurement, differential scanning calorimetric analysis (DSC) and transmission electron microscopy (TEM). T5 treated alloy showed the positive effect on the two-step aging at pre-aging temperatures between 273 and 343 K, unlike T6 treated alloy which showed the negative effect at pre-aging temperatures below 343 K. The positive effect on two-step aging seems to be the characteristic behavior at T5 heat treatment. Difference of two-step aging behavior between T5 and T6 treatments seems to result from the difference of cluster (1) formed in the pre-aging process below 343 K. Higher water-quenching temperature after casting tended to increase the hardness after artificial aging.
収録刊行物
-
- 軽金属
-
軽金属 61 (10), 507-512, 2011
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206339601280
-
- NII論文ID
- 10030513945
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DC%2BC3MXhsVehur%2FK
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 11284570
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可