- Crack Growth Characteristic and Damage Evaluation under Creep-Fatigue Interactive Condition for W-Added High-Cr Steel
- コウCr フェライトケイ タイネツコウ ノ クリープ ・ ヒロウ ジョウケン カ ニ オケル キレツ セイチョウ トクセイ ト ソンショウ ヒョウカ
この論文をさがす
抄録
Crack growth characteristic under the conditions of high temperature creep and fatigue interaction is dominated by cyclic dependent mechanism due to fatigue and time dependent mechanism due to the time of load application (creep). For many cases, this characteristic changes from the cyclic dependent to the time dependent mechanisms through an unstable transition region induced by creep and fatigue competitive mechanisms. To understand the physical mechanism of the interactive effects of creep and fatigue, it is important to clarify the damage mechanics around the crack. In the present study, the experiments of creep-fatigue crack growth tests and the quantitative analysis of damage by measuring Vickers hardness were conducted to understand the interactive effects of creep and fatigue on the crack growth characteristic. Additionally, by observing the material microstructure using EBSD, damage mechanisms were clarified. As a result, creep effect contributed to the expansion of damage region and fatigue effect increased the degree of damage. Interaction of these effects resulted in the occurrence of unstable transition region on the characteristic of creep-fatigue life.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 76 (11), 624-633, 2012
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報
-
- CRID
- 1390001206482594176
-
- NII論文ID
- 10031129950
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 024079425
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可