Evaluation of the caries-preventive effect of three orthodontic band cements in terms of fluoride release, retentiveness, and microleakage
-
- SHIMAZU Kisaki
- Department of Pediatric Dentistry, The Nippon Dental University School of Life Dentistry at Tokyo
-
- OGATA Kiyokazu
- Department of Pediatric Dentistry, The Nippon Dental University School of Life Dentistry at Tokyo Division of Dentistry, Tokyo Metropolitan Children's Medical Center
-
- KARIBE Hiroyuki
- Department of Pediatric Dentistry, The Nippon Dental University School of Life Dentistry at Tokyo
この論文をさがす
抄録
This in vitro study was undertaken to evaluate the caries-preventive effect of three orthodontic band cements (a dual-curing resinmodified glass ionomer cement [RMGIC] and two light-curing polyacid-modified composite resin [compomer] cements) in terms of fluoride release, retentiveness, and microleakage after thermocycling. The RMGIC (Ortholy Band Paste [GC Ortholy, Inc., Tokyo, Japan]) showed a significantly higher amount of cumulative fluoride release over 180 days (p<0.001) and significantly greater tensile bond strength (p<0.001) than the compomer cements (Transbond Plus [3M Unitek, Monrovia, CA, USA] and Ultra Band-Lok [Reliance Orthodontic Products, Inc., Itasca, IL, USA]). Its bond strength was unaffected by thermocycling (2,000 cycles), indicating good retentiveness, whereas that of the compomer cements significantly decreased after thermocycling. Moreover, it had lower dyepenetration scores, indicative of less microleakage. These findings suggest that the RMGIC may have a better caries-preventive effect than the compomer cements and is suitable for long-term orthodontic banding.
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 32 (3), 376-380, 2013
日本歯科理工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679694168832
-
- NII論文ID
- 10031158835
-
- NII書誌ID
- AA10443149
-
- COI
- 1:CAS:528:DC%2BC3sXhsVCns7zP
-
- ISSN
- 18811361
- 02874547
-
- PubMed
- 23718996
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- PubMed
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可