- Influence of the cation species in Cl<sup>-</sup> containing solution on corrosion of Al–Mg–Si alloy
- Al-Mg-Siケイ ゴウキン ノ フショク ニ オヨボス エンカブツ スイヨウエキ チュウ ノ カチオンシュ ノ エイキョウ
- Influence of the cation species in Cl- containing solution on corrosion of Al^|^ndash;Mg^|^ndash;Si alloy
この論文をさがす
抄録
In this work, the influence of cation species on the corrosion behavior of Al–Mg–Si alloy in Cl- containing solution was studied by immersion test and electrochemical measurement. The results of immersion test showed that severe pitting corrosion occurred at the Al-masking boundary of the sample and more weight loss of samples after immersion test gained in MgCl2 solution than those in NaCl and CaCl2 solutions. Anodic polarization curves showed little difference in pitting potential of Al–Mg–Si alloy in Cl- containing solutions regardless of the cation species. On the other hand, cathodic polarization curves showed the increase of cathodic current density in MgCl2 solution than those in NaCl and CaCl2 solutions. This electrochemical behavior suggested the remarkable corrosion of Al–Mg–Si alloy in MgCl2 solution was caused by the increase of cathodic reaction. The reason why the cathodic reaction increased in MgCl2 solution was considered that the pH at cathode surface was kept by buffering action of Mg2+ because of the less solubility of Mg (OH) 2.
収録刊行物
-
- 軽金属
-
軽金属 63 (5), 175-181, 2013
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681317359872
-
- NII論文ID
- 10031193248
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 024518274
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可