酸化物超伝導体の臨界電流密度におけるピーク効果 : 第2報 SmBa_2Cu_3O_<7-d> 超電導体における臨界電流密度の酸素量依存性

機関リポジトリ Web Site

書誌事項

タイトル別名
  • Peak Effects in Critical Current Densities of Oxide Superconductors
  • サンカブツ チョウデンドウタイ ノ リンカイ デンリュウ ミツド ニ オケル ピーク コウカ ダイ2ホウ SmBa2Cu3O7 d チョウデンドウタイ ニ オケル リンカイ デンリュウ ミツド ノ サンソリョウ イゾンセイ

この論文をさがす

抄録

Stoichiometric SmBa_2Cu_3O_<7-d> samples were prepared by a solid-state reaction method and showed peak effecs in their J_c-H characteristics. The oxygen contents of samples were determined by a coulometric titration method. A sample annealed at 350℃ for 40 hours has the highest peak effect in J_c. The oxygen content of the sample was 6.84,which was the lowest of the samples. The tetragonal phase in the orthorhombic phase was observed in the sample which had the most significant peak effect by TEM observation. On the other hand, the samples annealed for longer times had weaker peak effect. As results of microscopic observation and the TEM observation, a oxygen deficiency was considered to work as pinning centers at 77K and at around 1T to exhibit the peak effect.

Stoichiometric SmBa_2Cu_3O_<7-d> samples were prepared by a solid-state reaction method and showed peak effecs in their J_c-H characteristics. The oxygen contents of samples were determined by a coulometric titration method. A sample annealed at 350℃ for 40 hours has the highest peak effect in J_c. The oxygen content of the sample was 6.84,which was the lowest of the samples. The tetragonal phase in the orthorhombic phase was observed in the sample which had the most significant peak effect by TEM observation. On the other hand, the samples annealed for longer times had weaker peak effect. As results of microscopic observation and the TEM observation, a oxygen deficiency was considered to work as pinning centers at 77K and at around 1T to exhibit the peak effect.

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ