切削温度上昇を伴う断続切削時の切れ刃欠損発生の解析的予測(第1報)

DOI Web Site 被引用文献2件

書誌事項

タイトル別名
  • Analytical Prediction of Chipping Occurrence of Carbide Tool in Interrupted Turning Operation with Temperature Rise (1st Report)
  • 切削温度上昇を伴う断続切削時の切れ刃欠損発生の解析的予測-1-超硬合金の衝撃劣化過程と破壊応力に及ぼす温度の影響
  • セッサク オンド ジョウショウ オ トモナウ ダンゾク セッサクジ ノ キレハ
  • Effect of Temperature on Fracture Characteristics of Carbide Material and on Its Deterioration Process by Impact Repetition
  • 超硬合金の衝撃劣化過程と破壊応力に及ぼす温度の影響

この論文をさがす

抄録

Using the specially designed impact testing machine, the fracture characteristics of carbide material P 20 and its deterioration process by impact repetition are examined quantitatively under various temperature less than 800°C and under various impact duration. The main results obtained are as follows: (1) The fracture stress decreases with temperature increase, however the features of fracture are seen as a brittle one even at 800°C. (2) Both temperature and heating duration have no effect on the deterioration process by impact. The rate of deterioration depends on the impact stress and the number of impact but on the temperature. (3) Many small cracks or voids with random size and directions around WC particles in a sintered carbide are generated by both the cyclic uniaxial compressive and tensile impact, thus the isotropical deterioration may be expected in a carbide material. (4) The hypothesis for evaluation of the deterioration process by multiaxial stressing at any temperature less than 800°C is proposed.

収録刊行物

  • 精密工学会誌

    精密工学会誌 53 (10), 1589-1595, 1987

    公益社団法人 精密工学会

被引用文献 (2)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ