- Production of High Purity Silicon by Carbothermic Reduction of Silica Using AC-arc Furnace with Heated Shaft
- シャフトシキ アークロ オ モチイタ タンソ ネツ カンゲン ニ ヨル コウ
この論文をさがす
抄録
To produce inexpensive solar-grade silicon of high purity, a AC-arc furnace has been developed based on a thermodynamic consideration of carbothermic reduction of silica to metallic silicon. The furnace is featured by a closed type shaft and a hearth with arc electrodes and feeding nozzles. The carbon pellets as a reducing agent are fed from the top of the shaft, whereas silica powder is transferred to the hottest arc spot in the hearth. The resulting species of SiO and SiC, generated through the reactions of SiO2 + C →SiO + CO and SiO + 2C →SiC + CO, react in the lower part of the shaft to yield silicon, SiO+ SiC →2Si + CO. Melting silicon is accumulated in the hearth and pulled out from the tapping hole.<BR>The productivity has been about 2 kg/h and the silicon yield has been found to be typically 83%. Analyses have shown that the impurities in the silicon were below 0.1 ppmw for B, 12 ppmw for Fe and below 5 ppmw for the other elements. Single-crystalline solar cells fabricated starting from this silicon after purifications of decarburization and unidirectional solidification have recorded a conversion efficiency of 16.5%. This value was equivalent to that of solar cells made from semiconductor-grade silicon.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 77 (10), 1656-1663, 1991
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205182002560
-
- NII論文ID
- 110001481055
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 3730180
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可