Ni-22Cr-9Mo-5Fe-4Nb 超耐熱合金におけるγ″相の析出と成長 Precipitation and Growth of γ″Phase in a Ni-22Cr-9Mo-5Fe-4Nb Superalloy

この論文をさがす

著者

抄録

Hardening behavior due to precipitation of a Ni_3Nb(γ″) phase during aging was experimentally studied for a Ni-22Cr-9Mo-5Fe-4Nb alloy. The alloy was homogenized at 1373K for 3.6 ks and then quenched in water. The homogenized alloy was aged at temperatures between 894 and 1073K for up to 720 ks. The aging was also carried out at 893 to 1033K for up to 720 ks for the alloys cold rolled with reductions of 4, 10, 30 and 50% after the homogenization. The micro Vickers (MV) hardness test was made for the aged specimens. The microstructures of the specimens were observed by transmission electron microscopy (TEM). For the specimens without cold rolling, the MV hardness monotonically increases with increasing aging time at 893, 943 and 1073K. On the other hand, the MV hardness increases with increasing aging time and then reaches the maximum values at 36 and 72 ks at 993 and 1033K, respectively. In the specimens with the maximum values of the MV hardness, disk-like γ″precipitates with diameters of 30 to 35 nm were observed in a γ matrix. Coarsening of the γ″phase seems to obey the Ostwald ripening mechanism. The activation enthalpy for the coarsening was obtained to be 418 kJ/mol. For the specimens with cold rolling, over-aging is rather restrained due to fine γ″particles precipitated along dislocations.

収録刊行物

  • 鐵と鋼 : 日本鐡鋼協會々誌

    鐵と鋼 : 日本鐡鋼協會々誌 85(3), 241-248, 1999-03-01

    社団法人日本鉄鋼協会

参考文献:  17件中 1-17件 を表示

  • <no title>

    SUNDARARAMAN M.

    Mater. Sci. Forum 3, 273, 1985

    被引用文献1件

  • <no title>

    RAYMOND E. l.

    Trans. Metall. Soc. AIME 239, 1415, 1967

    被引用文献5件

  • <no title>

    PAULONIS D. F.

    Trans. Am. Soc. Met. 62, 611, 1969

    被引用文献6件

  • <no title>

    SIMS C. T.

    Superalloys II, High-temperature Materials for Aerospace and Industrial Power 97, 1987

    被引用文献1件

  • <no title>

    HAN Y.

    Met.Sci 16, 555, 1982

    被引用文献9件

  • <no title>

    KUSABIRAKI K.

    Tetsu-to-Hagane 84, 643, 1998

    被引用文献1件

  • <no title>

    KUSABIRAKI K.

    Tetsu-to-Hagane 76, 1341, 1990

    被引用文献9件

  • <no title>

    KUSABIRAKI K.

    Tetsu-to-Hagane 78, 650, 1992

    被引用文献7件

  • <no title>

    KUSABIRAKI K.

    Tetsu-to-Hagane 79, 1369, 1993

    被引用文献3件

  • <no title>

    KUSABIRAKI K.

    Tetsu-to-Hagane 80, 348, 1994

    被引用文献2件

  • <no title>

    KIRMAN I.

    Metall. Mater. Trans. 1, 2667, 1970

    被引用文献1件

  • <no title>

    RAGHAVAN M.

    Metall. Trans. A 8A, 1071, 1977

    被引用文献1件

  • <no title>

    CHATURVEDI M. C.

    Metall.Trans.A 10A, 1579, 1979

    被引用文献3件

  • <no title>

    KUSABIRAKI K.

    Tetsu-to-Hagane 82, 159, 1996

    被引用文献2件

  • <no title>

    金属学会

    金属データブック 25, 1974

    被引用文献1件

  • Morphology of γ" Precipitates in a Ni-15Cr-8Fe-6Nb Alloy

    KUSABIRAKI Kiyoshi , HAYAKAWA Itaru , OOKA Takayuki

    ISIJ international 36(1), 74-79, 1996-01-15

    J-STAGE 参考文献25件 被引用文献2件

  • <no title>

    KUSABIRAKI K.

    Metall. Trans. A 29A, 1169, 1998

    DOI 被引用文献1件

各種コード

  • NII論文ID(NAID)
    110001481913
  • NII書誌ID(NCID)
    AN00151251
  • 本文言語コード
    JPN
  • 資料種別
    ART
  • ISSN
    00211575
  • NDL 記事登録ID
    4667734
  • NDL 雑誌分類
    ZP42(科学技術--金属工学・鉱山工学--鉄鋼)
  • NDL 請求記号
    Z17-356
  • データ提供元
    CJP書誌  NDL  NII-ELS  J-STAGE 
ページトップへ