- Oxide Dispersion Strengthened Nickel and Nichrome by Means of the Spray-dispersion Method
- フンシャ ブンサンホウ ニヨル サンカブツ ブンサン キョウカ ニッケル オヨ
この論文をさがす
抄録
WO3, Al2O3, ZrO2, Y2O3 or ThO2-dispersed nickel and nichrome were produced by the "Spray-Dispersion Method", and their mechanical properties were studied. The main results obtained are summarized as follows:<BR>1) The addition of 1.6 pct. niobium as a "controlling element" was effective in lowering the oxide particle size in nickel. The mean diameter of ThO2 particles in nichel containing 1.6 pct. niobium reached to about 60 nm.<BR>2) 20 pct. of chromium in nickel also decreased the oxide particle size, and the addition of 0.8 pct. niobium in nickel-20 pct. chromium alloy decreased the mean diameter of Al2O3 particles to 79 nm.<BR>3) Tensile strengths at room temperature of oxide spray-dispersed nickels increased with the volume fraction of oxide particles and their increments were maintained even at 1073 K. In the case of oxide spray-dispersed nichromes, their incroments of tensile strength at room temperature were small, but those were multiplied at higher temperature.<BR>4) The fine oxide particles contributed to an increase of creep rupture strength, and this tendency became more pronounced toward longer time. 1273 K-1000 h creep rupture strength of 2 vol pct. ThO2 spray-dispersed nickel and 3.8 vol pct. Al2O3 spray-dispersed nichrome, for instance, were 47 Mpa and 19 Mpa, respectively.<BR>5) The oxidation resistance at high temperature of oxide spray-dispersed nickel and nichrome was improved as compared with non-dispersed ones.<BR>From these results, the oxide dispersion strengthened nickel-base heat-resisting alloy has been able to produce by the "Spray-Dispersion Method".
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 68 (8), 1024-1031, 1982
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205182487936
-
- NII論文ID
- 110001488996
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 2453978
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可